Table 1 Fabrication conditions of the PCL and ND/PCL fibrous matrices with varying ND concentration (0, 0.5, 1, 2, and 3 wt%). The fiber diameter of the PCL and ND/PCL fibrous matrices was determined using ImageJ® software

From: Fabrication and optimization of Nanodiamonds-composited poly(ε-caprolactone) fibrous matrices for potential regeneration of hard tissues

Groups

Fiber diameter (μm)

Voltage (kV)

Flow rate (mL/min)

PCL only

1.82 ± 0.12

10

0.008

ND 0.5 wt%

1.93 ± 0.13

8.5

0.02

ND 1 wt%

1.83 ± 0.16

8

0.03

ND 2 wt%

1.84 ± 0.25

7.5

0.03

ND 3 wt%

1.80 ± 0.24

6.5

0.03