Table 1: Electrospinning parameters of microfibrous PLGA fabrics

From: Lamination of microfibrous PLGA fabric by electrospinning a layer of collagen-hydroxyapatite composite nanofibers for bone tissue engineering

Polymer/

Solvent

Voltage

TCD distance

Flow rate

Syringe

Fiber diameter

PLGA 25 wt%

THF:DMF 3:1

12 kV

15 cm

1.5 mL/h

20G

5.2 ± 0.014 μm

PLGA 25 wt%

THF:DMF 3:1

15 kV

15 cm

1.5 mL/h

20G

3.6 ± 0.012 μm

PLGA 25 wt%

THF:DMF 3:1

18 kV

15 cm

1.5 mL/h

20G

3.4 ± 0.011 μm