Table 2 EDS analysis of CaP coatingsData are shown as mean ± standard deviation from n = 3 samples
From: Calcium phosphates and silicon: exploring methods of incorporation
| O (at%) | Ca (at%) | P (at%) | Si (at%) | ||
|---|---|---|---|---|---|
| Control | 45,33 ± 0,60 | 37,77 ± 0,46 | 16,87 ± 0,25 | ||
| CaP-A | 1 mM | 45,6 ± 0,35 | 36,1 ± 0,14 | 16,8 ± 0,42 | 1,50 ± 0,35 |
| 5 mM | 42,95 ± 0,35 | 39,05 ± 0,07 | 16,00 ± 0,07 | 2,00 ± 0,07 | |
| 10 mM | 44,6 ± 0,61 | 34,67 ± 0,85 | 12,73 ± 0,64 | 7,97 ± 0,89 | |
| 1 mM | 46,75 ± 0,07 | 35,95 ± 0,07 | 16,25 ± 0,07 | 1,00 ± 0,14 | |
| CaP-I | 5 mM | 42,83 ± 2,01 | 31,6 ± 2,18 | 14,07 ± 0,55 | 11,53 ± 0,59 |
| 10 mM | 51,35 ± 0,35 | 21,6 ± 1,27 | 9,05 ± 0,64 | 17,9 ± 1,56 | |